Stainless Steel Wire Mesh Raw Material 304 Stainless Steel:
304 stainless steel is a common material in stainless steel, with a density of 7.93 g/cm3, also known as 18/8 stainless steel in the industry. High temperature 800 degrees, with good processing performance, high toughness characteristics, widely used in industrial and furniture decoration industry and food and medical industries.
Physical properties:
Tensile strength σb (MPa) ≥ 520
Conditional yield strength σ0.2 (MPa) ≥ 205
Elongation δ5 (%)≥40
Reduction in area ψ (%) ≥ 60
Hardness: ≤187HBW; ≤90HRB; ≤200HV
Density (20°C,g/cm3):7.93
Melting point (°C): 1398~1454
Specific heat capacity (0~100°C, KJ·kgK): 0.50
Thermal conductivity (W·m·K): (100°C) 16.3, (500°C) 21.5
Linear expansion coefficient (10·K): (0~100°C) 17.2, (0~500°C) 18.4
Resistivity (20°C, 10Ω·m): 0.73
Longitudinal Elastic Modulus (20°C, KN/mm): 193
316 stainless steel:
316 stainless steel, 18Cr-12Ni-2.5Mo Due to the addition of Mo, its corrosion resistance, atmospheric corrosion resistance and high temperature strength are particularly good, and it can be used under harsh conditions; excellent work hardening (non-magnetic). Equipment for the use of seawater, equipment for production of chemicals, dyes, paper, oxalic acid, fertilizers; photography, food industry, coastal facilities, ropes, CD rods, bolts, nuts.
316 stainless steel chemical composition: C ≤ 0.08, Si ≤ 1.00, Mn ≤ 2.00, P ≤ 0.035, S ≤ 0.03, Ni: 10.0-14.0, Cr: 16.0-18.5, Mo: 2.0-3.0. 316 stainless steel mechanical properties, tensile Strength (Mpa) 620 MIN, Yield Strength (Mpa) 310 MIN, Elongation (%) 30 MIN, Area Reduction (%) 40 MIN, 316 Stainless Steel Density 8.03 g/cm3, Austenitic Stainless Steels generally use this value .
316l stainless steel:
316L stainless steel is commonly used in heat exchangers for pulp and paper equipment, dyeing equipment, film processing equipment, pipes, materials for building exteriors in coastal areas, as well as bracelets and cases for advanced watches. Marine equipment equipment, chemicals, dyes, paper, oxalic acid, fertilizers and other production equipment; photography, food industry, coastal facilities, ropes, CD rods, bolts, nuts.
1) The appearance of cold rolled products is good and beautiful;
2) Due to the addition of Mo, corrosion resistance, especially excellent resistance to pitting corrosion;
3) Excellent high temperature strength
4) Excellent work hardening (weak magnetic after processing)
5) Non-magnetic in solid solution state;

6)Relative to 304 stainless steel, the price is higher.chemical composition%:
C ≤ 0.03
Si ≤ 1.0
Ni: 10.0-14.0
Cr: 16.0-18.0